12 Rare Earth Magnets - Ring(Countersunk), 0.5" OD x 0.15" ID x 0.125" Th. |
Item: MAGNSN0590
Dimensions: (H x W x L) 0.0 x 0.0 x 0.0 |
Continue Shopping
|
|
NSN0590 12-Count
Rare Earth Magnets - Ring(Countersunk), 0.5 in. Outside Diameter x 0.15 in. Inside Diameter x 0.125 in. Thick, N,
Rare earth magnets are the strongest type of permanent magnet currently made. They are amazingly powerful for their size and have innumerable uses. These countersunk ring magnets are 0.500 inch (12.7mm) outside diameter, 0.150 inch (3.8mm) inside diameter and 0.125 inch (3.2mm) thick. They are magnetized through the thickness. They are composed of grade 40 neodymium iron boron magnetic material and are plated in nickel-copper-nickel for a shiny corrosion resistant finish. Maximum working temperature is 176 F (80 C).
SPECIFICATIONS:
Part Number: NSN0590
Imperial Dimensions: 0.5 inch outside diameter x 0.15 inch inside diameter x 0.125 inch thick
Metric Dimensions: 12.7mm outside diameter x 3.81mm inside diameter x 3.175mm thick
Material: Sintered Neodymium-Iron-Boron (NdFeB)
Shape: Ring
Plating: Ni-Cu-Ni (Nickel)
Magnetization Direction: Thickness
Grade: N40
Pull Force (lbs[g]): 3.2[1451]
Surface Field(G): 3531
Maximum Operating Temperature: 80 Deg C (176 Deg F)
Dimensional Tolerance: +/-0.005"
Magnet Quantity: 12
Volume (cm3): 0.37
Weight (g): 2.75
Brand: Magcraft
Packaging: Magpak Tube
UPC: 897970000860
Remanent Flux Density Br (kG [T]): 12.5-12.8 [1.25-1.28]
Coercivity HcB (kOe [kA/m]): >=10.9 [>=867]
Intrinsic Coercivity HcJ (kOe [kA/m]): >=12.0 [>=995]
Maximum Energy Product Bhmax (MGOe [kJ/m3]): 38-41 [302-326]
Density p(g/cm3): >=7.45
Compression Strength (Mpa): 600-1200
Bending Strength (Mpa): 150-380
Vickers Hardness (HV): 460-660
Recoil Permeability (urec): 1.05
Electrical Resistance (Ohm*mm2/m): 1.25-1.55
Curie Temperature Tc (°C): 310
Thermal Expansion Coefficient 100°C//(x10^-6/K): 6
Thermal Expansion Coefficient 100°C?(x10^-6/K): -1
|