NSN0683 Rare-Earth Disc Magnets, 0.75 in. Diameter x 0.0625 in. Thick, 10-Count
SPECIFICATIONS: These disc magnets are 0.75 inch (19.1mm) diameter and 0.063 inch (1.6mm) thick. They are magnetized through the thickness. They are composed of grade 40 neodymium iron boron magnetic material and are plated in nickel-copper-nickel for a shiny corrosion resistant finish. Their individual pull force is approximately 4 lbs. Maximum working temperature is 176 F (80 C).
Part Number NSN0683 Imperial Dimensions 0.75 inch diameter x 0.0625 inch thick Metric Dimensions 19.05mm diameter x 1.5875mm thick Material Sintered Neodymium-Iron-Boron (NdFeB) Shape Disc Plating Ni-Cu-Ni (Nickel) Magnetization Direction Thickness Grade N40 Pull Force (lbs[g]) 4[1814] Surface Field(G) 1899 Max. Operating Temperature 80 Deg C (176 Deg F) Dimensional Tolerance +/-0.005" Volume (cm3) 0.45 Weight (g) 3.39
Packaging Magpak Tube UPC 875661000832 Remanent Flux Density Br (kG [T]) 12.5-12.8 [1.25-1.28] Coercivity HcB (kOe [kA/m]) >=11.3 [>=923] Intrinsic Coercivity HcJ (kOe [kA/m]) >=12.0 [>=995] Maximum Energy Product Bhmax (MGOe [kJ/m3]) 38-41 [302-326] Density p(g/cm3) >=7.45 Compression Strength (Mpa) 600-1200 Bending Strength (Mpa) 150-380 Vickers Hardness (HV) 460-660 Recoil Permeability (urec) 1.05 Electrical Resistance (Ohm*mm2/m) 1.25-1.55 Curie Temperature Tc (°C) 310 Thermal Expansion Coefficient 100°C//(x10^-6/K) 6 Thermal Expansion Coefficient 100°C(x10^-6/K) -1
|